POM 900 美国杜邦 物性参数表

文章出处:网络转载网责任编辑:admin人气:-发表时间:2016-01-07 16:20

POM 900 美国杜邦物性表

牌号900
厂家(产地)美国杜邦
密度1.42 g/cm3
弯曲强度96 MPa
拉伸强度68 MPa
弯曲模量2960 MPa
材料供应佳进塑胶
缺口冲击强度69
POM 900 美国杜邦 技术数据
性能项目试验条件[状态]测试方法测试数据数据单位
密度 ASTM D-7921.42 
吸水量24hrs浸泡+73H(+23℃)ASTM D-5700.25%
吸水量浸泡均衡点+73H(+23℃)ASTM D-5700.90%
吸水量Equil.50%R.h.+73H(+23℃)ASTM D-5700.22%
弯曲疲劳忍耐限度+23℃ASTM D-67131.7MPa
扩散因数+73H(+23℃)106HzASTM D-1500.005 
线性热膨胀系数+85 to +140HASTM D-6966.810-5in/in.H
弹性系数+73HASTM D-638450MPsi
负载下之变形2000psi@+122H(14Mpa@50℃)ASTM D-6210.5%
弯曲降服强度+73HASTM D-79014.0MPsi
断裂时之拉力伸张度+212H(+100℃)ASTM D-638>260%
伸张强度-55℃ASTM D-638101MPa
伸张强度+250HASTM D-6383.8MPsi
弯曲疲劳忍耐限度+73HASTM D-6714.6MPsi
IZOD冲击强度40℃ASTM D-25653.4j/m
拉力冲击抵抗力+73HASTM D-182270ft.lb/in2
无切口冲击程度+73HASTM D-25616ft.lb/in
断裂时之拉力伸张度-68H(-55℃)ASTM D-63810%
伸张强度+100℃ASTM D-63835.9MPa
IZOD冲击强度-40HASTM D-2561.0ft.lb/in
压缩应力+73H@1%ASTM D-ef.ASTM D-6955.0MPsi
伸张强度-68HASTM D-63814.7MPsi
挠曲系数+158H在25℃下240MPsi
无切口冲击程度+23℃ASTM D-256850j/m
伸张强度+212HASTM D-6385.2MPsi
压缩应力+73H@10%ASTM D-ef.ASTM D-69517.6MPsi
挠曲系数+250H在25℃下90MPsi
IZOD冲击强度+23℃ASTM D-25669.4j/m
伸张强度+158HASTM D-6386.9MPsi
弯曲降服强度+23℃ASTM D-79096.5MPa
拉力冲击抵抗力+23℃ASTM D-1822150kj/m2
压缩应力+23℃@1%ASTM D-ef.ASTM D-69534.5MPa
弹性系数+23℃ASTM D-6383100MPa
伸张强度+23℃ASTM D-63868.9MPa
洛氏硬度 ASTM D-785M94 R120 
挠曲系数+70℃在25℃下1655MPa
挠曲系数+122℃在25℃下620MPa
挠曲系数+23℃在25℃下2960MPa
伸张强度+73HASTM D-63810.0MPsi
热传导系数BTU-in/hr 2.6 
挠曲系数+73H在25℃下430MPsi
断裂时之拉力伸张度+73H(+23℃)ASTM D-63825%
伸张强度+122℃ASTM D-63826.2MPa
摩擦系数+73H(+23℃)静态ThrustWasherTest30.20 
挠曲系数-55℃在25℃下4140MPa
断裂时之拉力伸张度+158H(+70℃)ASTM D-638180%
压缩应力+23℃@10%ASTM D-ef.ASTM D-695121MPa
剪力+23℃ASTM D-73265.5MPa
断裂时之拉力伸张度+250H(+122℃)ASTM D-638>260%
挠曲系数+212H在25℃下140MPsi
伸张强度+70℃ASTM D-63847.5MPa
挠曲系数+100℃在25℃下965MPa
摩擦系数+73H(+23℃)动态ThrustWasherTest30.35 
挠曲系数-68H在25℃下600MPsi
IZOD冲击强度+73HASTM D-2561.3ft.lb/in
绝缘强度Short Time 90 milsASTM D-149500V/mil
绝缘系数+73H(+23℃)102to106HzASTM D-1503.7 
绝缘强度Short Time 2.3mmASTM D-14919.7MV/m
电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.
电阻系数+73H(+23℃)0.2%H2OASTM D-2571015ohm-cm
线性热膨胀系数+140 to +220HASTM D-6967.610-5in/in.H
熔点 ASTM D-2133347H
线性热膨胀系数+220 to +300HASTM D-6968.310-5in/in.H
热变形温度1.8MPaASTM D-648136
线性热膨胀系数-40 to +85HASTM D-6965.810-5in/in.H
热传导系数W/mk 0.37 
线性热膨胀系数+104 to +150℃ASTM D-69614.910-5m/m.℃
热变形温度0.5MPaASTM D-648172
线性热膨胀系数+60 to +104℃ASTM D-69613.710-5m/m.℃
线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃
熔点 ASTM D-2133175
热变形温度264psiASTM D-648277H
热变形温度66psiASTM D-648342H
可燃烧性 UL-9494HB 
线性热膨胀系数-40 to +29℃ASTM D-69610.410-5m/m.℃

 