POM 150SA 美国杜邦 物性参数表

文章出处:网络转载网责任编辑:admin人气:-发表时间:2016-01-07 17:50
POM 150SA 美国杜邦 技术数据
性能项目试验条件[状态]测试方法测试数据数据单位
密度 ASTM D-7921.42 
吸水量浸泡均衡点+73℉(+23℃)ASTM D-5700.90%
吸水量24hrs浸泡+73℉(+23℃)ASTM D-5700.25%
吸水量Equil.50%R.h.+73℉(+23℃)ASTM D-5700.22%
扩散因数+73℉(+23℃)106HzASTM D-1500.005 
断裂时之拉力伸张度+158℉(+70℃)ASTM D-638230230
弹性系数+23℃ASTM D-6383100MPa
无切口冲击程度+73℉ASTM D-256>100(no break)ft.lb/in
断裂时之拉力伸张度+212°F(+100℃)ASTM D-638>260%
拉力冲击抵抗力+23℃ASTM D-256>5300(no break)j/m
伸张强度+100℃ASTM D-63835.9MPa
摩擦系数+73℉(+23℃)静态ThrustWasherTest30.20 
负载下之变形2000psi@+122℉(14Mpa@50℃)ASTM D-6210.5%
压缩应力+73℉@10%Def.ASTM D-69518.0MPsi
断裂时之拉力伸张度-68℉(-55℃)ASTM D-63838%
伸张强度+122℃ASTM D-63826.2MPa
断裂时之拉力伸张度+73℉(+23℃)ASTM D-63875%
挠曲系数-55℃在25℃下3650MPa
热变形温度66psiASTM D-648342
IZOD冲击强度40℃ASTM D-25696.1j/m
挠曲系数+250℉在25℃下90MPsi
伸张强度+250℉ASTM D-6383.8MPsi
压缩应力+23℃@1%Def.ASTM D-69535.9MPa
伸张强度+23℃ASTM D-63868.9MPa
压缩应力+23℃@10%Def.ASTM D-695124MPa
剪力+73℉ASTM D-7329.5MPsi
挠曲系数+158℉在25℃下225MPsi
IZOD冲击强度-40℉ASTM D-2561.8ft.lb/in
挠曲系数+23℃在25℃下2620MPa
IZOD冲击强度+73℉ASTM D-2562.3ft.lb/in
挠曲系数+70℃在25℃下1550MPa
压缩应力+73℉@1%Def.ASTM D-6955.2MPsi
伸张强度-68℉ASTM D-63814.7MPsi
剪力+23℃ASTM D-73265.5MPa
弯曲降服强+23℃ASTM D-79098.6MPa
拉力冲击抵抗力+23℃ASTM D-1822350kj/m2
弯曲疲劳忍耐限度+73℉ASTM D-6714.7MPsi
洛氏硬度 ASTM D-785M94,R120 
伸张强度+158℉ASTM D-6386.9MPsi
断裂时之拉力伸张度+250℉(+122℃)ASTM D-638>260%
挠曲系数+122℃在25℃下620MPa
挠曲系数+100℃在25℃下895MPa
弯曲降服强+73℉ASTM D-79014.3MPsi
伸张强度-55℃ASTM D-638101MPa
挠曲系数-68℉在25℃下530MPsi
挠曲系数+212℉在25℃下130MPsi
伸张强度+70℃ASTM D-63847.5MPa
弹性系数+73℉ASTM D-638450MPsi
伸张强度+212℉ASTM D-6385.2MPsi
热传导系数  2.6BTU-in/hr
热变形温度1.8MpaASTM D-648136
IZOD冲击强度+23℃ASTM D-256123j/m
拉力冲击抵抗力+73℉ASTM D-1822170ft.lb/in2
弯曲疲劳忍耐限度+23℃ASTM D-67132.4MPa
摩擦系数+73℉(+23℃)动态ThrustWasherTest30.35 
热变形温度264psiASTM D-648277
挠曲系数+73℉在25℃下380MPsi
伸张强度+73℉ASTM D-63810.0MPsi
绝缘强度Short Time,2.3mmASTM D-14919.7MV/m
绝缘系数+73℉(+23℃)102to106ASTM D-1503.7 
电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.
电阻系数+73℉(+23℃)0.2%H2OASTM D-2571015ohm-cm
绝缘强度Short Time,90 milsASTM D-149500V/mil
熔点 ASTM D-2133175
线性热膨胀系数+140 to +220℉ASTM D-6967.610-5in/in.℉
可燃烧性 UL-9494HB 
热传导系数  0.37W/mk
熔点 ASTM D-2133347
线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃
线性热膨胀系数+85 to +140℉ASTM D-6966.810-5in/in.°F
线性热膨胀系数+60 to +104℃ASTM D-69613.710-5m/m.℃
线性热膨胀系数-40 to +29℃ASTM D-69610.410-5?m/m.℃
热变形温度0.5MpaASTM D-648172
线性热膨胀系数+85 to +140℉ASTM D-6966.810-5in/in.℉
线性热膨胀系数+104 to +150℃ASTM D-69614.910-5m/m.℃
线性热膨胀系数-40 to +85℉ASTM D-6965.810-5in/in.℉
线性热膨胀系数+220 to +300℉ASTM D-6968.310-5in/in.℉

 