POM 900F 美国杜邦 物性表参数

文章出处:网络转载网责任编辑:admin人气:-发表时间:2016-01-07 16:37

POM 900F 美国杜邦物性表

牌号900F
厂家(产地)美国杜邦
密度1.42 g/cm3
硬度120
材料供应商佳进塑胶
拉伸强度66 MPa
弯曲模量2760 MPa
缺口冲击强度69
POM 900F 美国杜邦 技术数据
性能项目试验条件[状态]测试方法测试数据数据单位
密度 ASTM D-7921.42 
吸水量浸泡均衡点+73H(+23℃)ASTM D-5701.40%
吸水量Equil.50%R.h.+73H(+23℃)ASTM D-5700.28%
吸水量24hrs浸泡+73H(+23℃)ASTM D-5700.32%
压缩应力+23℃@1%Def.ASTM D-69531.0MPa
伸张强度+122℃ASTM D-63822.8MPa
伸张强度+100℃ASTM D-63829.6MPa
挠曲系数-68H在25℃下570MPsi
洛氏硬度 ASTM D-785M92 R120 
挠曲系数+23℃在25℃下2760MPa
伸张强度+250HASTM D-6383.3MPsi
挠曲系数+73H在25℃下400MPsi
IZOD冲击强度-40HASTM D-2561.0ft.lb/in
断裂时之拉力伸张度+250H(+122℃)ASTM D-638>260%
绝缘强度Short Time 90 milsASTM D-149500V/mil
负载下之变形[email protected]+122H([email protected]ASTM D-6210.7%
弯曲降服强度+23℃ASTM D-79093.8MPa
剪力+73HASTM D-7329.5MPsi
挠曲系数+250H在25℃下80MPsi
伸张强度-55℃ASTM D-63896.5MPa
伸张强度+73HASTM D-6389.7MPsi
挠曲系数-55℃在25℃下3930MPa
伸张强度+212HASTM D-6384.3MPsi
扩散因数+73H(+23℃)106HzASTM D-1500.005 
挠曲系数+158H在25℃下220MPsi
剪力+23℃ASTM D-73265.5MPa
IZOD冲击强度+73HASTM D-2561.3ft.lb/in
挠曲系数+122℃在25℃下550MPa
挠曲系数+70℃在25℃下1515MPa
IZOD冲击强度40℃ASTM D-25653.4j/m
伸张强度-68HASTM D-63814.0MPsi
压缩应力[email protected]%Def.ASTM D-6954.5MPsi
弹性系数+73HASTM D-638450MPsi
IZOD冲击强度+23℃ASTM D-25669.4j/m
挠曲系数+212H在25℃下130MPsi
伸张强度+158HASTM D-6386.6MPsi
压缩应力+23℃@10%Def.ASTM D-695108MPa
弹性系数+23℃ASTM D-6383100MPa
伸张强度+23℃ASTM D-63866.9MPa
弯曲疲劳忍耐限度+23℃ASTM D-67127.6MPa
断裂时之拉力伸张度+158H(+70℃)ASTM D-638150%
弯曲降服强度+73HASTM D-79013.6MPsi
断裂时之拉力伸张度+212H(+100℃)ASTM D-638>260%
挠曲系数+100℃在25℃下895MPa
压缩应力[email protected]%Def.ASTM D-69515.6MPsi
摩擦系数+73H(+23℃)动态ThrustWasherTest30.20 
伸张强度+70℃ASTM D-63845.5MPa
弯曲疲劳忍耐限度+73HASTM D-6714.0MPsi
断裂时之拉力伸张度+73H(+23℃)ASTM D-63825%
电阻系数+73H(+23℃)0.2%H2OASTM D-2571015ohm-cm
绝缘系数+73H(+23℃)102to106HzASTM D-1503.7 
绝缘强度Short Time 2.3mmASTM D-14919.7MV/m
电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.
线性热膨胀系数-40 to +85HASTM D-6965.810-5in/in.H
热变形温度264psiASTM D-648266H
热变形温度66psiASTM D-648328H
线性热膨胀系数+220 to +300HASTM D-6968.310-5in/in.H
线性热膨胀系数-40 to +29℃ASTM D-69610.410-5m/m.℃
可燃烧性 UL-9494HB 
线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃
线性热膨胀系数+60 to +104℃ASTM D-69613.710-5
线性热膨胀系数+104 to +150℃ASTM D-69614.910-5m/m.℃
线性热膨胀系数+85 to +140HASTM D-6966.810-5in/inH
熔点 ASTM D-2133175
线性热膨胀系数+140 to +220HASTM D-6967.610-5in/in.H
热变形温度1.8MPaASTM D-648130
热变形温度0.5MPaASTM D-648170
熔点 ASTM D-2133347H
可燃烧性 UL-9494HB


 